性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
热性能
|
热变形温度 |
|
ASTM D648 |
90 |
℃ |
维卡软化点 |
|
ASTM D-1525 |
|
℃(℉) |
热变形温度(退火) |
6.4mm 18.6kg/cm2
|
ASTM D-648 |
|
℃(℉) |
机械性能
|
伸长率 |
|
ASTM D-638 |
30 |
% |
弯曲模量 |
23℃ |
ASTM D-790 |
24000 |
kg/cm? |
缺口冲击强度 |
23℃ 1/8in(3.2mm) |
ASTM D-256 |
26 |
kg.cm/cm |
缺口冲击强度 |
|
ASTM D256 |
208 |
J/m |
洛氏硬度 |
|
ASTM D785 |
110 |
R |
拉伸强度 |
|
ASTM D638 |
51 |
Mpa |
弯曲强度 |
23℃ |
ASTM D-790 |
650 |
kg/cm? |
其它性能
|
阻燃性 |
|
GB 4609 |
- |
级 |
物理性能
|
比重 |
|
ASTM D-792 |
1.04 |
23/23℃ |
熔体流动速率 |
200℃ 5kg(条件G) |
ASTM D-1238 |
4.5 |
g/10min |
熔体流动速率 |
|
ASTM D1238 |
30 |
g/10min |
模塑收缩率 |
|
ASTM D-955 |
0.4-0.7 |
% |
|